Verila Lithium HD
Heavy Duty - High Performance - Extreme Pressure (EP) - Multipurpose Lithium Grease
Verila Lithium HD is lubricating grease based on lithium 12-hydroxystearate soap and high-quality mineral base oil of ISO VG220 viscosity grade. It is available in NLGI 0, NLGI 1 and NLGI 2 consistency grades as VERILA Lithium HD 0, VERILA Lithium HD 1 and VERILA Lithium HD 2 respectively. The grease contains carefully balanced antioxidants, rust and corrosion inhibitors and EP/AW additives as well as water resistance and mechanical stability improvers.
- Excellent Mechanical Stability prevents from leakage.
- Very Good Water Resistance and Rust Inhibiting Properties.
- High Load Carrying Capacity and strong lubricating film.
- Very Good Oxidation Stability.
- Very Good Pumpability, even at low temperatures.
Recommended for lubrication under high loads in both industrial and automotive applications: all kinds of general applications in transport, agriculture and off-road equipment; lubrication of plain and rolling bearings exposed to severe operating conditions and hostile environments; NLGI 0 and NLGI 1 grades are especially recommended for centralized lubrication systems of excavators.
|ISO 6743-9||L-XCCEB 0||L-XCCHB 1||L-XCCHB 2|
|Test Parameter||Test Method||Value|
|Appearance||Visual||Smooth and Homogenous|
|Base Oil Viscosity at 40 Celsius, mm2/s||ISO 3104||200|
|NLGI Grade||ASTM D217||0||1||2|
|Operating Temperature Range||-30 to 130 Celsius|
|Cone Penetration, Worked, 0.1 mm||ISO 2137||355– 385||310 – 340||265 – 295|
|Cone Penetration, after 10 000 cycles, 0.1 mm||ISO 2137||<20|
|Roll Stability, Penetration change, %||ASTM D1831||<10|
|Dropping Point||ISO 6299||> 180 Celsius||> 185 Celsius||> 195 Celsius|
|Rust Test, EMCOR||ISO 11007||0-0|
|Four-Ball EP Test, Weld Point, N||ASTM D2596||3150|
|Water Resistance Test||DIN 51 807-1||Max. 1-90|
|Water Washout Test at 79º C, wt % loss||ISO 11009||6.5% Typical|
While the information and figures given here are typical of current production and compliant with VERILA specification, minor variations may occur